Coverage CORROSION Lectures in Fracture Mechanics - PowerPoint Presentation

1. CoverageCORROSIONLectures in Fracture MechanicsNational Institute of Technology Tiruchirappalli

2. What is Corrosion?Corrosion is defined as deterioration or destruction of material due to its interaction with environment. It’s a reverse of metallurgy.Any material when It is kept in a certain atmosphere their will be potential difference between the material and the surroundings. To complete the circuit ions of material comes to the solution.CORROSION RATE: Rate at which ions are coming out.

3. Principle of CorrosionIt is based on Electrochemical Reaction .Reaction is as follows OXIDATION (Anodic Reaction) Zn Zn2+ +2e- REDUCTION (Cathodic Reaction) Hydrogen Evolution 2H+ + 2e- H2 Oxygen Reduction O2 + 4H+ + 4e- 2H20

4. Principle of Corrosion

5. Different Types of Corrosion

6. Galvanic or Two-metal CorrosionGalvanic Effect – If two dissimilar materials are in a contact (electrically connected or physical contact), one will be undergo corrosion (act as a anode) in the presence of corrosive medium (electrolyte).The metal with high standard oxidation potential act as a anode and other with low reduction potential act as a cathode. Galvanic effect can be estimated from EMF series and galvanic series of materials .

7. Galvanic Corrosion Mechanism Reaction is as follows At anode Fe Fe2+ + 2e- At Cathode acidic medium (Hydrogen Evolution type) 2H+ + 2e- H2 Oxygen Reduction O2 + 4H+ + 4e- 2H20 Alkaline or Neutral medium(oxygen absorption type)½ O2 + H2O +2e- 2OH- Fe2+ + 2OH- Fe(OH)2 4Fe(OH)2 + O2 Fe(OH)3

8. Examples of Galvanic Corrosion Anodic- cathodic behavior of steel with zinc and tin outside layers exposed to the Atmosphere.

9. Prevention from Galvanic Corrosion Avoid contact between dissimilar metals.For unavoidable situations anodic area should be larger than the cathodic area. the two metals should be as close as possible in the galvanic series. an insulator may be fitted between the two metals. avoid threaded joints between the metals.

10. Localized CorrosionLocalised Corrosion is the selective removal of metal by corrosion at a small area or zones on a metal surface in contact with corrosive environment It takes place at a higher rate than the rest of original surface. Occurs when corrosion works with other destructive process such as stress , fatigue , erosion and other forms of chemical attack.

11. Chemical factor:Initiated in the metal- intergranular, pittingInitiated in the environment- creviceChemical and mechanical factors:Mechanical process in metal-stress corrosion cracking, hydrogen embrittlementMechanical action of metal-erosion corrosionMechanical action of solid body of metal-fretting corrosionLocalized Corrosion…

12. Crevice corrosion: Corrosion that occurs in stagnant locations such as those found under gaskets. Filiform corrosion: Corrosion that occurs when water gets under a coating such as paint.Pitting corrosion: The creation of small holes in the surface of a metal.Intergranular corrosion: Where the boundaries of crystallites of the material are more susceptible to corrosion than their insides.Localized Corrosion…

13. Intergranular CorrosionIntergranular corrosion (IGC) is a selective attack in the vicinity of the grain boundaries of a stainless steel. It is as a result of chromium depletion, mainly due to the precipitation of chromium carbides in the grain boundaries.

14. Crevice Corrosion Electrochemical oxidation-reduction (redox) process It occurs within localized volumes of stagnant solution(like dust) trapped in pockets, corners or rivet heads.Crevice corrosion is much more dangerous than uniform corrosion.Crevice corrosion is highly accelerated if chloride, sulphate or bromide ions are present in the electrolyte solution.Mechanism of crevice corrosion is similar to that of Pitting corrosion: dissolution of the metal and gradual acidification of the electrolyte caused by its insufficient aeration (Oxygen penetration). 

15. Crevice Corrosion: MechanismAnodic reaction :- Fe = Fe2+ + 2e- (dissolution of iron)Cathodic reaction :-1/2O2 + H2O + 2e- = 2(OH-)Hydrolysis :-FeCl2 + 2H2O = Fe(OH)2 + 2HCl

16. Prevention from Crevice Corrosion Use butt joint instead of lap-joints.Clean thoroughly to remove stagnant.Avoid sharp corner while designingUse non-absorbable solid gaskets such as Teflon.

17. Filiform CorrosionIt is a special type of crevice corrosion. Here the corrosion takes place under a thin film . It appears on the steel , Magnesium and Aluminium surface covered by tin, silver, gold phosphates, etc. The corrosion appears as thread-like filaments under the coating.

18. Filiform Corrosion mechanismThe mechanism has a number of characteristics that are similar to Crevice corrosion, e.g. differential aeration and hydrolysis of metal ions resulting in increasing acidity in the region of dissolution.

19. According to this theory, corrosion on the surface of a metal is due to direct reaction of atmospheric gases like oxygen, halogens, oxides of Sulphur, oxides of nitrogen, hydrogen sulfide and fumes of chemicals with metal.The extent of corrosion of a particular metal depends on the chemical affinity of the metal towards reactive gas.Oxygen is mainly responsible for the corrosion of most metallic substances when compared to other gases and chemicals.Mainly three types: (1) Oxidation corrosion (Reaction with oxygen) (2) Corrosion by other gases. (3) electrochemicalAtmospheric Corrosion

20. Some of the metals directly react with oxygen in the absence of moisture. Alkali and alkaline earth metals react with oxygen at room temperature and form corresponding oxides, while some metals react with oxygen at higher temperature. Metals like Ag, Au and Pt are not oxidized as they are noble metals.Oxidation Corrosion

21. During oxidation of a metal, metal oxide is formed as a thin film on the metallic surface which protects the metal from further corrosion. If diffusion of either oxygen or metal is across this layer, further corrosion is possible. Thus, the layer of metal oxide plays an important role in the process of corrosion.Oxides of Pb, Al and Sn are stable and hence inhibit further corrosion. They form a stable, tightly adhering oxide film.In case of porous oxide film, atmospheric gases pass through the pores and react with the metal and the process of corrosion continues to occur till the entire metal is converted into oxide.Porous oxide layer is formed by alkali and alkaline earth metals. Molybdenum forms a volatile oxide film of MoO3 and accelerates corrosion.Au, Ag, Pt form unstable oxide layer which decomposes soon after the formation, thereby preventing further corrosion.

22. In dry atmosphere, these gases react with metal and form corrosion products which may be protective or non-protective. Dry Cl2 reacts with Ag and forms AgCl which is a protective layer, while SnCl4 is volatile. In petroleum industries at high temperatures, H2S attacks steel forming FeS scale which is porous and interferes with normal operations.CORROSION BY OTHER GASES

23. Stress Corrosion CrackingStress corrosion occurs due to tensile stresses (applied and residual stresses) on the susceptible material in the presence of a specific corrosive environment, resulting In the formation of propagating cracks.

24. Causes of SCCBasic ChloridesAcid ChloridesNH3Ammonia CompoundsAlkalisNitratesRollingDrawingAnnealingBendingWelding Due to certain metal forming processes probability of SCC will increase.

25. Mechanism of SCC

26. Active Path DissolutionActive path dissolution is a material failure due to stress corrosion cracking (SCC) that is characterized by the progression of corrosion along an intermolecular path of least resistance with high concentrations of tensile strength.Active path dissolution is characterized by the significantly increased rate of corrosion along an intergranular sub-section or boundary that presents above average susceptibility to corrosion. Such granular boundaries on the molecular level within metals tend to display segregation of impure elements, while the bulk layer of the material contains a passive tendency. This makes it more difficult for passivation and protection of the bulk material. occur.

27. Film Induced Cleavage

28. PreventionControl over operating temperature.Control stresses while machining.Avoid specific chemical environment.Choose an inert material, that does not reacts with the specific environment.

29. Pitting CorrosionPitting corrosion is a localized attack in the metal resulting in the formation of pit, hole, cavity. (confined to a point or small area)Reason:– When the anodic area is small and cathodic area is large, it leads to drastic corrosion at the anode to form a pit or a hole.

30. PittingPitting is intermediate stage between general overall corrosion and complete corrosion resistance.

31. Causes of PittingDamage/cracking of protective film over the metal.Scratches / cut edges.Sliding under loads.Chemical Attack (Chloride damages the protective oxide layer)Surface Roughness.Turbulent flow of fluid over metal.

32. Pit Shape and GrowthPits usually grow in direction in gravity.Lesser number start on vertical surface and rarely do they grow upward.Pits tend to undermine or undercut the surface as they grow.Subsurface damage is much more severe than is indicated by surface appearances.Pitting requires an extended initiation period , once started pit penetrates at an ever increasing rate.

33. Mechanism of Pit FormationAt the interface between the pit and the adjacent surface, iron hydroxide forms due to interaction between the OH- produced by cathodic reaction and pit corrosion product.This is further oxidised by the dissolved oxygen in the solution to Fe(OH)3 , Fe304 and other oxides.This rust rim grows in the form of a tube.

34. Environmental FactorsMost pitting corrosions are caused by chloride and chloride containing ions.Most pitting is associated with halide ions, with chlorides, bromides and hypo chlorites being the most prevalent.Fluorides and Iodides have comparatively little pitting tendencies.Even most corrosion resistant alloys can be pitted by Copper Chlorides and Iron Chlorides.

35. Biological Corrosion The interaction of organisms with corrosion processes, is a complex subject encompassing contributions from several disciplines ranging from chemistry and surface science to microbiology and bacteriology.They are caused by microbes and fungi.Aerobic bacteria decreases the concentration of oxygen in the medium in contact with the metal surface.The main product of corrosion is Iron Sulphide.

36. Hydrogen Embrittlement is the degradation of structural properties of solid due to hydrogen.Primary impact on the metals takes the form of loss of ductility and reduced load carrying capacity.This is often a result of accidental introduction of hydrogen during forming and finishing operations.Occurs in most metal, but not usually in copper, gold, silver and tungsten.HYDROGEN EMBRITTLEMENT

37. During hydrogen embrittlement, hydrogen is introduced to the surface of a metal and individual hydrogen atoms diffuse through the metal.Solubility of hydrogen increases at higher temperatures, raising the temperature can increase the diffusion of hydrogen.If there is significantly more hydrogen outside the metal than inside, hydrogen diffusion can occur even at lower temperatures.Individual hydrogen atoms within the metal gradually recombine to form hydrogen molecules, creating pressure from within the metal.This pressure can increase to levels where the metal has reduced ductility, toughness, and tensile strength, up to the point where it cracks open(Hydrogen induced cracking –HIC).

38.

39. THEORIESHYDROGEN EMBRITTLEMENTThe absorption of hydrogen decreases the atomic binding forces of the metal lattice.This results in the premature brittle-material fracture along the grain boundaries or network levels.The absorption of hydrogen decreases the surface free energy of the metal.Propagation of the crack tip is enhanced.Explains crack propagation of high-strength steels in low-pressure hydrogen environments.Occurs when metals are charged with hydrogen during solidification.High-pressure hydrogen can form in micro voids.Same mechanism as hydrogen blistering.

40. OccurrencesHydrogen embrittlement can occur during various manufacturing operations or operational use anywhere that the metal comes into contact with atomic or molecular hydrogen.Processes that can lead to this include cathodic protection, pickling, phosphating and electroplating.

41. Preventive Measures Prevention in Design:High-strength metals and alloys are more susceptible to embrittlement.Common mistake is to overcompensate on strength requirements for service.At ambient conditions: Minimize the stress acting on the material!

42. Prevention in processing:Embrittlement can originate from poor production techniques.Problems arise when hydrogen is allowed into production environment.Remedies: Maintain low hydrogen atmosphereHeat treatmentPreventive Measures…

43. Prevention in Welding:Embrittlement can be localized around a weld.Welding rods containing hydrogen are the source.Remedies:Low hydrogen welding rods stored in a dry placeLocal heat treatment before & after weldingPreventive Measures…

44. Using Clean Steal:Rimmed steel tend to have numerous voids.Substitution of killed steel greatly increases the resistance to hydrogen interstitials for embrittlement. Because of less number of voids in this material. Preventive Measures…

45. Reducing Corrosion Rate:Hydrogen embrittlement occurs frequently during pickling operations.Where corrosion of the base metal produces vigorous hydrogen evolution.By adding inhibitor, base metal corrosion can be eliminated during pickling by subsequent decrease in hydrogen pickup.Preventive Measures…

46. Baking:Hydrogen embrittlement is an almost reversible process, especially in steels.If hydrogen is removed, the mechanical properties of treated material are almost equal to Hydrogen free steel.Common way of removing hydrogen in steel is by baking at low temperatures at 200-300 Fo.Preventive Measures…

47. Substituting Alloys:High strength steels are more susceptible to hydrogen embrittlement.Alloying with Ni or Mo reduces susceptibility.Nickel containing steel and Nickel base alloys have very low hydrogen diffusion rates.Best way to prevent from hydrogen embrittlement.Preventive Measures…

48. TestingThere are two ASTM standards for testing embrittlement due to hydrogen gas. Standard Test Method for Determination of the Susceptibility of Metallic Materials to Hydrogen Gas Embrittlement (HGE):- Uses a diaphragm loaded with differential pressure.If hydrogen containing environment at high pressure , high temperature, or both:- Uses a cylindrical tensile specimen tested into an enclosure pressurized with hydrogen or helium.

49. ExampleIn 2013, six months prior to opening, the East Span of the Oakland Bay Bridge failed during testing. Catastrophic failures occurred in shear bolts in the span, after only two weeks of service, with the failure attributed to embrittlement, possibly from the environment.

50. Corrosion PreventionMaterial SelectionDesignAlteration of Environment Coating Cathodic ProtectionElectroplatingHot Dipping GalvanisingTinning

51. Most important method:– Generally people believe that SS is good , but in chlorine containing medium and stressed structures , these are more susceptible than ordinary steels. Localised such as Pitting and Crevice corrosion attack more on SS than MS .General combination of alloy and medium for better resistance is given below :-SS – Nitric AcidTin – Distilled WaterSteel – Conc. Sulphuric Acid and many more……Material Selection

52. As riveted joints are sites for crevice corrosion, welding is preferred more than riveting tanks.Excessive mechanical stresses or residual stresses are avoided to reduce stress corrosion cracking.Eliminate electrical contact between dissimilar to prevent galvanic corrosion by using similar material or using insulate materials.Avoid sharp bends in piping systems when high velocities abrasion materials are involved to prevent erosion corrosion.Tank bottoms must be designed in some inclination towards holes for easy draining otherwise the left out liquids results in severe corrosion.Design

53. Altering the corrosive environment by reducing the aggressiveness of the medium with added inhibitors.Changing the medium:- lowering the temperature, decreasing velocity, removing oxygen and changing concentrations.Different inhibitors are:-Adsorption inhibitors:- organic compounds which adsorb metal surface and decrease the metal dissolution and reduction reactions.Scavengers inhibitors (sodium sulphite and hydrazine):- remove dissolved oxygen from water solutions.Hydrogen-evolutions poisons (arsenic and antimony ions):- reduce hydrogen evolution reaction and effective in acidic solutions.Altering of Environment

54. Metallic or inorganic & organic coatings!Metallic coating can be applied easily very easily and they are quite deformable. eg:-silverware, galvanized steel, tin cans.Inorganic coating are to be applied by diffusion or chemical conversion and these are brittle. eg:- chromized steel, anodized aluminiumOrganic coating protect more than the metallic coating on a tonnage basis. Eg:-paints, varnishes, lacquers.Coatings

55. Metal to be protected is forced to act as cathode so that corrosion does not occur.The principle is that supplying the electrons to metal through electrolyte.Cathodic Protection

56. Electroplating is a process of coating a superior metal over the base metal(inferior metal) by passing direct current through the electrolyte containing the soluble salt of the coating metal.Electroplating

57. It is the process of coating the base metal (metal with higher melting point ) dipping into a bath containing molten coating metal (metal with low melting point).It is of two types:- (A) galvanising (anodic coating) :- coating of more active metal, Zn over Cu. (B) tinning (Cathodic Coating):- coating of less active material, Tin over Cu.Hot Dipping

58. Prevention and Control of CorrosionCorrosion prevention techniques can be generally classified into 6 groups:Environmental ModificationsMetal Selection and Surface ConditionsCathodic ProtectionCorrosion InhibitorsCoatingPlating

59. Environmental Modification- Methods to reduce the sulfur, chloride or oxygen content in the surrounding environment can limit the speed of metal corrosion.For example, feed water for water boilers can be treated with softeners or other chemical media to adjust the hardness, alkalinity or oxygen content in order to reduce corrosion on the interior of the unit.Metal Selection and Surface Conditions- Proper monitoring and the elimination of unnecessarily vulnerable surface conditions, along with taking steps to ensure that systems are designed to avoid reactive metal combinations and that corrosive agents are not used in the cleaning or maintenance of metal parts are all also part of effective corrosion reduction program.The development of new alloys, designed to protect against corrosion in specific environments are constantly under production. Nickel alloys and titanium alloys are all examples of alloys designed for corrosion prevention.

60. Cathodic Protection- This method, known as a sacrificial system, uses metal anodes, introduced to the electrolytic environment, to sacrifice themselves (corrode) in order to protect the cathode.In a sacrificial system, metallic ions move from the anode to the cathode, which leads the anode to corrode more quickly than it otherwise would. As a result, the anode must regularly be replaced.Example: Using Mg blocks in ships

61. Corrosion Inhibitors- Corrosion inhibitors are chemicals that react with the metal's surface or the environmental gasses causing corrosion, thereby, interrupting the chemical reaction that causes corrosion.The effectiveness of a corrosion inhibitor depends on fluid composition, quantity of water, and flow regime.A common mechanism for inhibiting corrosion involves formation of a coating, often a passivation layer, which prevents access of the corrosive substance to the metalVolatile amines are used in boilers to minimize the effects of acid.Corrosion inhibitors are often added to paints.

62.

63. Coatings- Paints and other organic coatings are used to protect metals from the degradative effect of environmental gasses.Anti-corrosion coatings allow for added protection of metal surfaces and acts as a barrier to inhibit the contact between chemical compounds or corrosive materials.Ceramic coatings - Ceramic coatings provide corrosion, erosion and thermal protection.Polymer coatings - Polymer coatings/paints are composed of binders (major polymer constituent of the coating), solvents (water or Hydrocarbon solvents) for viscosity control, pigments and additives (eg., Corrosion inhibitors).Oil and grease coating

64. Plating- Metallic coatings, or plating, can be applied to inhibit corrosion as well as provide aesthetic, decorative finishes.There are four common types of metallic coatings: 1-Electroplating: A thin layer of metal - often nickel, tin, or chromium - is deposited on the substrate metal (generally steel) in an electrolytic bath. The electrolyte usually consists of a water solution containing salts of the metal to be deposited. 2-Hot dipping: When immersed in a molten bath of the protective, coating metal a thin layer adheres to the substrate metal.

65. 3-Electroless plating: also known as chemical or auto-catalytic plating, is a non-galvanic plating method that involves several simultaneous reactions in an aqueous solution.It is mainly different from electroplating by not using external electrical power. In the manufacture of printed circuit boards, electroless plating is used to form the conductive part. The non-conductive part is treated with palladium catalyst and then made conductive by electroless copper plating

66. 4-Mechanical plating: also known as peen plating, mechanical deposition, or impact platingIt is a plating process that imparts the coating by cold welding fine metal particles to a workpiece.It is commonly used to overcome hydrogen embrittlement problems. Commonly plated workpieces include nails, screws, nuts, washers, stampings, springs, etc.

67. ProcessThe process begins with a descaling and removing soil from the workpiece. After cleaning, the parts are prepared by combining them with water, medium, and a surface conditioner. The surface conditioner lightly coats the workpiece in copper, while the medium removes any residual mill scale or oxides. Finally, accelerators, promoters and metal powder are added to the mix. The accelerators and promoters provide the proper chemical environment for the plating to occur, such as the maintenance of a pH level of 1 to 2 to prevent oxidation and promote adhesion. The medium that is already in the mixture cold welds the metal powder to the workpiece through impacts that are induced by the tumbling action of the tumbler (Due to the rotation of tumbler)The surface finish can be improved with a water polish. The time required for the above process is approximately 50 minutes.